Removal of arsenate and arsenite from aqueous solution by waste cast iron
Nag-Choul Choi , Song-Bae Kim , Soon-Oh Kim , Jae-Won Lee , Jun-Boum Park
DOI:10.1016/S1001-0742(11)60786-9
Received April 25, 2011,Revised June 10, 2011, Accepted , Available online April 06, 2012
Volume 24,2012,Pages 589-595
The removal of As(III) and As(V) from aqueous solution was investigated using waste cast iron, which is a byproduct of the iron casting process in foundries. Two types of waste cast iron were used in the experiment: grind precipitate dust (GPD) and cast iron shot (CIS). The X-ray diffraction analysis indicated the presence of Fe0 on GPD and CIS. Batch experiments were performed under different concentrations of As(III) and As(V) and at various initial pH levels. Results showed that waste cast iron was effective in the removal of arsenic. The adsorption isotherm study indicated that the Langmuir isotherm was better than the Freundlich isotherm at describing the experimental result. In the adsorption of both As(III) and As(V), the adsorption capacity of GPD was greater than CIS, mainly due to the fact that GPD had higher surface area and weight percent of Fe than CIS. Results also indicated the removal of As(III) and As(V) by GPD and CIS was influenced by the initial solution pH, generally decreasing with increasing pH from 3.0 to 10.5. In addition, both GPD and CIS were more effective at the removal of As(III) than As(V) under given experimental conditions. This study demonstrates that waste cast iron has potential as a reactive material to treat wastewater and groundwater containing arsenic.