Effect of oxide nanoparticles on the morphology and fluidity of phospholipid membranes and the role of hydrogen bonds
Xiaoran Wei , Junchao Yu , Lei Ding , Jingtian Hu , Wei Jiang
DOI:10.1016/j.jes.2017.02.011
Received December 09, 2016,Revised February 05, 2017, Accepted February 17, 2017, Available online March 01, 2017
Volume 29,2017,Pages 221-230
Engineered oxide nanoparticles (NPs) are widely applied in insulators, catalyzers, paints,cosmetic products, textiles and semiconductors. Their attachment on cell membrane may lead to cytotoxicity. The effects of Al 2 O 3 , Fe 2 O 3 , SiO 2 , TiO 2 and ZnO NPs on membrane integrity and fluidity were studied using giant or small unilamellar vesicles in this study. Al 2 O 3 and SiO 2 NPs disrupted the oppositely charged membrane, indicating the important role of electrostatic attraction. However, Fe 2 O 3 , TiO 2 and ZnO NPs did not cause serious membrane disruption as Al 2 O 3 and SiO 2 NPs. Membrane fluidity was evaluated by the generalized polarity (GP) values of Laurdan fluorescent emission. SiO 2 NPs induce the membrane gelation of both positively and
negatively charged membrane. Al 2 O 3 and ZnO NPs induced the gelation of the oppositely charged membrane, but did not cause obvious membrane gelation to the like charged membrane. The phospholipid molecular structural changes after NP exposure were analyzed by Fourier transform infrared (FT-IR) spectroscopy. FT-IR spectra revealed the hydrogen bond formation between NPs and the carbonyl/phosphate groups of phospholipids. Al 2 O 3 and SiO 2 NPs showed strongest evidence of hydrogen bonding on their FT-IR spectra. It was consistent with the microscopic observation and fluorescent data that Al 2 O 3 and SiO 2 NPs caused more serious membrane disruption and gelation.This study on membrane damageprovides further knowledge on the cytotoxicity of nanomaterials and the safety of NP application.